Observation time | Gelation strength mPa·s | |
Polymer concentration 0.2% | Polymer concentration 0.3% | |
3 d | 9506 | 13,175 |
4 d | 9389 | 13,001 |
5 d | 9174 | 12,817 |
6 d | 9025 | 12,680 |
7 d | 8869 | 12,530 |
8 d | 8700 | 12,342 |
9 d | 8573 | 12,209 |
10 d | 8432 | 12,077 |
11 d | 8301 | 11,935 |
12 d | 8182 | 11,801 |
13 d | 8060 | 11,675 |
14 d | 7927 | 11,538 |
15 d | 7799 | 11,414 |
16 d | 7708 | 11,347 |
17 d | 7698 | 11,304 |
30 d | 7672 | 11,278 |